2008 | 6 | 2 | 289-295
Article title

Structural and electrical properties of KCa2Nb5O15 ceramics

Content
Title variants
Languages of publication
EN
Abstracts
EN
A polycrystalline sample of KCa2Nb5O15 with tungsten bronze structure was prepared by a mixed oxide method at high temperature. A preliminary structural analysis of the compound showed an orthorhombic crystal structure at room temperature. Surface morphology of the compound shows a uniform grain distribution throughout the surface of the sample. Studies of temperature variation on dielectric response at various frequencies show that the compound has a transition temperature well above the room temperature (i.e., 105°C), which was confirmed by the polarization measurement. Electrical properties of the material have been studied using a complex impedance spectroscopy (CIS) technique in a wide temperature (31–500°C) and frequency (102–106 Hz) range that showed only bulk contribution and non-Debye type relaxation processes in the material. The activation energy of the compound (calculated from both the loss and modulus spectrum) is same, and hence the relaxation process may be attributed to the same type of charge carriers. A possible ‘hopping’ mechanism for electrical transport processes in the system is evident from the modulus analysis. A plot of dc conductivity (bulk) with temperature variation demonstrates that the compound exhibits Arrhenius type of electrical conductivity.
Contributors
  • Department of Physics and Meteorology, IIT, Kharagpur, 721 302, India
  • P.G. Department of Physics, Sambalpur University, Sambalpur, 768 019, India
author
References
  • [1] G. Goodman, J. Am. Ceram. Soc. 36, 368 (1953) http://dx.doi.org/10.1111/j.1151-2916.1953.tb12820.x[Crossref]
  • [2] M.H. Francombe, B. Lewis, Acta Crystallog. 11, 696 (1958) http://dx.doi.org/10.1107/S0365110X58001882[Crossref]
  • [3] G.A. Smolenskii, A.I. Agranovskaya, Dokl. Akad. Nauk. SSSR. 97, 237 (1954)
  • [4] S. Sakamoto, T. Yazaki, Appl. Phys. Lett. 22, 429 (1973) http://dx.doi.org/10.1063/1.1654700[Crossref]
  • [5] A. Liu, M. Lee, L. Hesselink, J. Opt. Soc. Am. B Opt. Phys. 17, 542 (2000) http://dx.doi.org/10.1364/JOSAB.17.000542[Crossref]
  • [6] C. Li, R. Guo, A.S. Bhalla, Ferroelectrics 339, 103 (2006) http://dx.doi.org/10.1080/00150190600738071[Crossref]
  • [7] G. Burns, F.H. Dacol, R. Guo, A.S. Bhalla, Appl. Phys. Lett. 57, 543 (1990) http://dx.doi.org/10.1063/1.104246[Crossref]
  • [8] T.R. Shrout, H. Chen, L.E. Cross, Ferroelectrics 74, 317 (1987)
  • [9] D. Szwagierczak, J. Kulawik, J. Eur. Ceram. Soc. 24, 1979 (2004) http://dx.doi.org/10.1016/S0955-2219(03)00358-3[Crossref]
  • [10] L. Fang, L. Chen, H. Zhang, C.L. Diao, R.Z. Yuan, Mat. Lett. 58, 2654 (2004) http://dx.doi.org/10.1016/j.matlet.2004.03.042[Crossref]
  • [11] X.M. Chen, Y. Yuan, Y.H. Sun, J. Appl. Phys. 97, 074108 (2005)
  • [12] G. Burns, F.H. Dacol, Phys. Rev. B 40, 4012 (1984) http://dx.doi.org/10.1103/PhysRevB.30.4012[Crossref]
  • [13] J. Ravez, H. El Alaoui-Belghiti, M. Elaatmani, A. Simon, Mater. Lett. 47, 159 (2001) http://dx.doi.org/10.1016/S0167-577X(00)00228-7[Crossref]
  • [14] B. Behera, P. Nayak, R.N.P. Choudhary, Mater. Lett. 61, 3859 (2007) http://dx.doi.org/10.1016/j.matlet.2006.12.048[Crossref]
  • [15] B. Behera, P. Nayak, R.N.P. Choudhary, Phys. Status Solidi A 204, 2479 (2007) http://dx.doi.org/10.1002/pssa.200622592[Crossref]
  • [16] P.R. Das, R.N.P. Choudhary, B.K. Samantray, Mater. Chem. Phys. 101, 228 (2007) http://dx.doi.org/10.1016/j.matchemphys.2006.04.005[Crossref]
  • [17] E. Wu, POWD, An Interactive Powder Diffraction Data Interpretation and Indexing Program, Ver. 2.1, School of Physical Sciences, Flinders University South Bedford Park, SA 5042 Australia
  • [18] E.A. Geiss, B.A. Scott, G. Burns, D.F. O’Kane, A. Segmuller, J. Amer. Ceram. Soc. 52, 276 (1969) http://dx.doi.org/10.1111/j.1151-2916.1969.tb09183.x[Crossref]
  • [19] H.P. Klug, L.E. Alexander, X-ray Diffraction Procedures, (Wiley, Chichester, UK, 1974) 966
  • [20] M.L.N. Goswami, R.N.P. Choudhary, P.K. Mahapatra, Ferroelectr. 216, 1 (1998) http://dx.doi.org/10.1080/00150199808018223[Crossref]
  • [21] J.R. MacDonald, Impedance Spectroscopy (Wiley, New York, 1987)
  • [22] R.N.P. Choudhary, Dillip K. Pradhan, C.M. Tirado, G.E. Bonilla, R.S. Katiyar, Phys. Status Solidi B 244, 2254 (2007) http://dx.doi.org/10.1002/pssb.200642344[Crossref]
  • [23] A.K. Jonscher, Nature 267, 673 (1977) http://dx.doi.org/10.1038/267673a0[Crossref]
  • [24] D.K. Pradhan, B.K. Samantaray, R.N.P. Choudhary, Awalendra K. Thakur, Mater. Sci. Eng. B-Solid 116, 7 (2005) http://dx.doi.org/10.1016/j.mseb.2004.08.009[Crossref]
  • [25] J. Plocharski, W. Wieczoreck, Solid State Ionics, 28–30, 979 (1988) http://dx.doi.org/10.1016/0167-2738(88)90315-3[Crossref]
  • [26] F. Borsa, D.R. Torgeson, S.W. Martin, H.K. Patel, Phy. Rev. B 46, 795 (1992) http://dx.doi.org/10.1103/PhysRevB.46.795[Crossref]
  • [27] I.M. Hodge, M.D. Ingram, A.R. West, J. Electroanal. Chem., 74, 125 (1976) http://dx.doi.org/10.1016/S0022-0728(76)80229-X[Crossref]
  • [28] D.C. Sinclair, A.R. West, J. Appl. Phys. 66, 3850 (1989) http://dx.doi.org/10.1063/1.344049[Crossref]
  • [29] P.B. Macedo, C.T. Moynihan, R. Bose, Phys. Chem. Glasses, 13, 171 (1972)
  • [30] A.K. Jonscher, Dielectric Relaxation in Solids (Chelsea Dielectrics, London, 1983)
Document Type
Publication order reference
Identifiers
YADDA identifier
bwmeta1.element.-psjd-doi-10_2478_s11534-008-0030-4
JavaScript is turned off in your web browser. Turn it on to take full advantage of this site, then refresh the page.