Synthesis of functional magnetic porous SrFe12O19/P(St-DVB-MAA) microspheres by a novel suspension polymerization

Content
Title variants
Languages of publication
EN
Abstracts
EN
In this study, a novel and effective suspension polymerization has been employed to prepare functional magnetic porous SrFe12O19/P(St-DVB-MAA) microspheres in the presence of bilayer surfactants (sodium dodecyl benzene sulfonate (SDBS) and oleic acid (OA)) coated on micro-size magnetic SrFe12O19. This was achieved by pre-polymerizing the organic phase, which contained co-monomers, porogens and treated magnetic particles, at 65°C for 0.5 h under ultrasound conditions. Aqueous solutions containing a dispersion agent were then added to effect suspension polymerization. Scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), thermogravimetric analysis (TGA) and magnetic property measurement system (MPMS) were used to characterize the functional magnetic porous microspheres. The results show that the microparticles are well shaped with a uniform size distribution of about 0.5 ∼ 0.7 mm and the surfaces of the microspheres have many micro-pores with an average diameter of 0.533 µm. There are carboxyl groups (−COOH) on the surface of the microspheres to the extent of 0.65 mmol g−1, as determined by conductometric titration. According to the XRD spectra, iron oxide consists mainly of SrFe12O19 which reveals hexahedral structure. The content of magnetic SrFe12O19 reaches 17.81% (by mass), and the microspheres have good heat resistance. The magnetic porous microspheres are ferromagnetic with high residual magnetization and coercivity, 21.59 emu g−1 and 4.13 kOe, respectively. The saturation magnetisation is around 42.85 emu g−1. [...]
Publisher
Journal
Year
Volume
6
Issue
4
Pages
627-633
Physical description
Dates
published
1 - 12 - 2008
online
28 - 10 - 2008
References
  • [1] X. B. Ding, Z. H. Sun, G. X. Wan, Y. Y. Jiang, React Funct Polym. 38, 11 (1998) http://dx.doi.org/10.1016/S1381-5148(97)00154-5[Crossref]
  • [2] J. Ugelstad, A. Berge, T. Ellingsen, Prog Polym Sci. 17, 526 (1992) http://dx.doi.org/10.1016/0079-6700(92)90017-S[Crossref]
  • [3] P. J. Robinson, P. Dunnil, M. D. Lilly, Biotech Bioeng. 15, 603 (1973) http://dx.doi.org/10.1002/bit.260150318[Crossref]
  • [4] J. D. Ding, F. S. Luo, G. C. Yang, J Huaihai Inst Technol. 10, 36 (2001)
  • [5] S. M. L. C. De, M. C. A. M. Leite, M. A. S. Costa, Mater Lett. 58, 3001 (2004) http://dx.doi.org/10.1016/j.matlet.2004.05.028[Crossref]
  • [6] B. Akkaya, L. Uzun, F. Candan, A. Denizli, Materials Science and Engineering: C 27, 180 (2007) http://dx.doi.org/10.1016/j.msec.2006.04.009[Crossref]
  • [7] P. Xue, H. F. Liu, Acta Polymerica Sinica 1, 64 (2007)
  • [8] H. Yanuz, S. S. Çelebi, Journal of Bioactive and Compatible Polymer 16, 221 (2001) http://dx.doi.org/10.1106/D0HM-XE5H-YBEH-V2Q2[Crossref]
  • [9] S. Akgol, A. Denizli, J. Molecular Catalysis B: Enzymatic 28, 7 (2004) http://dx.doi.org/10.1016/j.molcatb.2003.12.010[Crossref]
  • [10] M. Odabasi, N. Ozkayar, S. Ozkara, S. Unal, A. Denizli, J. Chromatogr. A 826, 50 (2005)
  • [11] B. Akkaya, L. Uzun, F. Candan, A. Denizli, Mater. Sci. Eng. C. 27, 180 (2007) http://dx.doi.org/10.1016/j.msec.2006.04.009[Crossref]
  • [12] C. D. S. M. Luiz, C. A. M. L. Marcia, A. S. C. Marcos, M. S. R. José, F. S. Lilian, R. S. Manoel, Materials Letters 58, 3001 (2004) http://dx.doi.org/10.1016/j.matlet.2004.05.028[Crossref]
  • [13] L. C. Santa Maria, M. A. S. Costa, J. G. M. Soares, S. H. Wang, M.R. Silva, Polymer 46, 11288 (2005) http://dx.doi.org/10.1016/j.polymer.2005.09.055[Crossref]
  • [14] J. B. Jun, S. Y. Uhm, J. H. Ryu, K. D. Suh, Colloids and Surfaces A: Physicochem. Eng. Aspects 260, 157 (2005) http://dx.doi.org/10.1016/j.colsurfa.2005.03.020[Crossref]
  • [15] G. L. Qiu, Y. L. Li, K. Zhao, Enzyme and Microbial Technology 39, 770 (2006) http://dx.doi.org/10.1016/j.enzmictec.2005.12.013[Crossref]
  • [16] T. Mitrelias, J. Palfreyman, Z. Jiang, J. Llandro, J. A. C. Bland, R. M. Sanchez-Martin, M. Bradley, J Magn. Magn. Mater. 310, 2862 (2007) http://dx.doi.org/10.1016/j.jmmm.2006.11.131[Crossref]
  • [17] X.Q. Liu, Z.Y. Ma, J.M. Xing, H.Z. Liu, J. Magn. Magn. Mater. 270, 1 (2004) http://dx.doi.org/10.1016/j.jmmm.2003.07.006[Crossref]
  • [18] X.Q. Liu, M.D. Kaminski, Y. P. Guan, H. T. Chen, H. Z. Liu, A. J. Rosengart, J Magn. Magn. Mater. 306, 248 (2006) http://dx.doi.org/10.1016/j.jmmm.2006.03.049[Crossref]
  • [19] C.S. Lin, C.C. Hwang, T.H. Huang, G.P. Wang, C.H. Peng, Materials Science and Engineering B 139, 24 (2007) http://dx.doi.org/10.1016/j.mseb.2007.01.053[Crossref]
  • [20] C.H. Yan, et al., J. Appl. Polym. Sci. 40, 89 (1990) http://dx.doi.org/10.1002/app.1990.070400108[Crossref]
  • [21] J. Wang, C. Zeng, Journal of Crystal Growth 270, 729 (2004) http://dx.doi.org/10.1016/j.jcrysgro.2004.07.012[Crossref]
Document Type
Publication order reference
YADDA identifier
bwmeta1.element.-psjd-doi-10_2478_s11532-008-0055-y
Identifiers
JavaScript is turned off in your web browser. Turn it on to take full advantage of this site, then refresh the page.